WC-10Ni
WC-10Ni
WOCO identifies this item as WC-10Ni, model / grade WC-10Ni. The source size is -140+270 mesh.
Specifications & website prices
| Specification | Original website price | MOQ |
|---|---|---|
| -140+270 mesh | $42.00 /KgOriginal page #legacy-878 ↗ | 100 Kg |
Each price retains the specification, currency and unit of its source listing. Confirm current availability and delivery with WOCO.
Product overview
WC-10Ni · Product description & applications
Model-level information transcribed from the WOCO product overview. Listed applications are examples; suitability and coating qualification depend on your process. Reference grades are separate from the priced specifications above.
- Agglomerated & sintered gray/black spherical or near-spherical particles, with good flowability.
- The maximum operating temperature is 500℃.
- Hard and dense coating, wear-resistant particle wear, fretting wear, adhesive wear, corrosion wear, erosion wear;
- Non-magnetic material
- Ni has higher corrosion resistance than Co, and is suitable for (moisture) wet corrosion environment;
- Mainly used in oilfield equipment, petrochemical industry, ball valve (oxidation environment), plate valve, offshore equipment and parts etc.
Grade specifications from the product overview
| Grade | Particle size | T.C % | Ni % | Fe % | O % | Process | Apparent density (g/cm³) | Hall flowability (s/50g) |
|---|---|---|---|---|---|---|---|---|
| FA119-2 | 20–53 µm | 5.3-5.8 | 9.0-11.0 | ≤0.2 | ≤0.5 | Agglomerated & Sintered | ≥4 g/cm³ | ≤18 s/50g |
| FA120-5 | 20–45 µm | 5.3-5.8 | 9.0-11.0 | ≤0.2 | ≤0.5 | Agglomerated & Sintered | ≥4 g/cm³ | ≤18 s/50g |
| FA121-3 | 15–45 µm | 5.3-5.8 | 9.0-11.0 | ≤0.2 | ≤0.5 | Agglomerated & Sintered | ≥4 g/cm³ | ≤18 s/50g |
| FA122-6 | 11–45 µm | 5.3-5.8 | 9.0-11.0 | ≤0.2 | ≤0.5 | Agglomerated & Sintered | ≥4 g/cm³ | ≤18 s/50g |
| FA123-7 | 10–38 µm | 5.3-5.8 | 9.0-11.0 | ≤0.2 | ≤0.5 | Agglomerated & Sintered | ≥4 g/cm³ | ≤18 s/50g |
| FA124-8 | 10–30 µm | 5.3-5.8 | 9.0-11.0 | ≤0.2 | ≤0.5 | Agglomerated & Sintered | ≥4 g/cm³ | ≤18 s/50g |
HVOF process reference & reported coating results
The following values belong to the stated process setup in the product overview. They are starting references, not a guarantee for other equipment, substrates, grades or production runs.
Reference process conditions
| Powder | WC-10Ni |
|---|---|
| Process type | Agglomerated & Sintered |
| Particle size | 45-15 µm |
| Spraying gun | JP5000 |
| Gun barrel | 4 inch |
| Kerosene | 24 L/h |
| Oxygen | 900 L/min |
| Carrier gas | 8.5 L/min |
| Powder feed rate | 80-100 g/min |
| Spraying distance | 340-380 mm |
Coating results in the overview
| Hardness | 1050-1250 HV0.3 |
|---|---|
| Bonding strength | ＞70 MPa |
| Deposition efficiency | 45-55 % |
| Porosity | ＜1 % |
Technical documents
Batch reports apply to the identified batch. Ask WOCO for documents relating to your order.
Product images & original specifications
- Product Name
- WC-10Ni
- Category
- Thermal spraying
- Product Size
- -140+270 mesh
- Tolerance
- 0
- MOQ
- 100Kg
Available specifications & supply reference
Original listing information is preserved below. Stock, delivery and freight are subject to current confirmation.
These are dated supplier listings. Their original prices and validity periods are shown for reference; ask WOCO for a current quotation.
| Specification | Packaging | Listing date / validity |
|---|---|---|
| -140+270 mesh | On request | 2017-08-01 · 180days |
Original supply details
- Origin
- CHINA
- Validity
- 180days
- Area
- CHINA
- Post date
- 2017-08-01