devoted to produce and sell tungsten carbide around the world

Our customer from all over the world,Any questions,please contact:jiang@wococarbide.com

Products Catalog

Inquire

Name*
E-mail*
Message*
 

Manufacturing method of ZR-NI alloy powder


Chengdu WOCO carbide Industry Co.,Ltd

     which was established in the hometown of hard metal of China--- ChengDu city in Sichuan province. A professional Chinese manufacturer of tungsten carbide products such as drawing die,indexable inserts shims, drilling bits, drawing dies, cold forging dies, carbide bars, carbide rods, carbide balls, carbide burrs, etc. Along with our company growth, we hope to build business with more companies abroad

Why choose our manufacturing method of zr-ni alloy powder

  • We have more than 10 years experience in manufacturing manufacturing method of zr-ni alloy powder products
  • Ex-factory is at least 30% cheaper than you own native
  • The quality conforms to the international ISO standards ,the service life of the product is long
  • The various types of products are in stock,the production cycle is short delivery time is within 4 days
  • Free samples can be provided
  • Small orders can be acceptable
  • We can make it according to your requirements or drawings.,OEM or ODM is acceptable.

Customer samples and drawings are also welcomed!

A manufacturing method of a Zr Ni alloy powder and its characteristics is treated with strong heat zirconyl chloride powder or zirconia powder, metal nickel powder (or its oxide powder) as raw material, calcium metal particle (or calcium hydride) as a reducing agent mixed mass material, placed in a high-temperature furnace,in an inert atmosphere, controlling the temperature between 950 to 1350 DEG C, constant temperature is maintained for 1 to 5 hours and water and the treatment of the product after high temperature reduction of diffusion, removing impurities, Zr Ni alloy powder.
Its characteristic is that the zirconium oxychloride and strong heat treatment conditions: zirconium oxychloride in air temperature between 300 DEG C to 1000 DEG C, the heating time control within 1 to 2 hours, income white loose block product by crushing and grinding into the alloy powder below 100 mesh.
Natural restoration of soaking treatment and calcium zirconium zirconium zirconium chloride calcium and the aim of nickel nickel zirconium oxygen and strong heat treatment of zirconium chloride powder or zirconia powder and metal powder (or its oxide powder) in the proportion of molecules in the stoichiometric ratio are the same; reducing agent of metal particle (or calcium hydride) dosage for reducing to strong heat treatment of oxygen or oxygen into the metal (as well as the reduction of nickel oxide to metallic nickel) required the theoretical value of 1.2 to 2.0 times; raw material mixture to fully mix building blocks or close heap. Water treatment is to use pure water or below 3% hydrochloric acid, the solution pH value cannot be less than 6.4, solution to remove impurities and alloy powder form.

manufacturing method of zr-ni alloy powder quality control

  • all raw material are tested in terms of density, hardness and T.R.S before use.
  • There are strict inspection on process and final products.
  • every batch of product can be traced.
If you have any other question or inquiry of manufacturing method of zr-ni alloy powder, please feel free to contact us through the following methods:  Mr.Jiang : jiang@wococarbide.com Mobile: 0086-138-0806-0309 Tel: 0086-28-8555-5525-803


 
Previous:Advantages and disadvantages of alloy powder coating Next:Cr3C2 - NiCr high-temperature wear-resistant spray powder
Powered by  Chengdu WOCO Carbide Industry Co., Ltd  ©2004-2014 www.wococarbide.net